Bottom price Uhp Electrodes - UHP Grades Graphite Electrodes – Sungraf

Product Detail

Product Tags

Feedback (2)

Like a result of ours specialty and repair consciousness, our enterprise has won a superb popularity amid buyers everywhere in the environment for Crystalline Flake Graphite, Furnace Electrodes, Electrolysis Of Graphite, All products are manufactured with advanced equipment and strict QC procedures in order to ensure high quality. Welcome customers new and old to contact us for business cooperation.

Bottom price Uhp Electrodes - UHP Grades Graphite Electrodes – Sungraf Detail:

Products Details

The electrodes carry the electricity that heats electric arc furnaces, the vast majority steel furnaces. They are made from petroleum coke after it is mixed with petroleum pitch, extruded and shaped, then baked to sinter it, and then graphitized by heating it above the temperature (3000 °C) that converts carbon to graphite. They can vary in size up to 11 ft. long and 30 in. in diameter.

UHP Grades Graphite Electrodes (1)

Usage

01
An increasing proportion of global steel is made using electric arc furnaces
02
The electric arc furnace itself is getting more efficient and making more steel per tonne of electrode

Typical properties of UHP graphite electrodes

Applicable Furmace Dia Property		AC Furnace			DC Furnace
Applicable Furmace Dia Property		300-400mm 12″～16″	450-500mm 18″～20″	550-600mm 22″～24″	650-700mm 24″～28″
Bulk Density	g/cm³	1.65～1.76	1.64～1.75	1.64～1.75	1.64～1.75
Specific Resistance	μΩM	4.2～6.0	4.2～6.0	4.2～6.0	4.2～5.5
Elastic Modulus	Gpa	7～14	7～14	7～14	7～14
Elastic Modulus	kgf/mm²	700～1,400	700～1,400	700～1,400	700～1,400
Flexural Strength	MPa	10.5～15	10～15	10～15	10～15
	kgf/cm²	105～150	100〜150	100-150	100～150
	N/cm²	1,050～1,500	1,000～1,500	1,000～1,500	1,000～1,500
Coefficient Of Thermal Expansion (R.T.≤600℃)	X10~-6/℃	1.0～1.5	1.0～1.5	1.0～1.5	1.0～1.4
Real Density	g/cm³	2.20～2.23	2.20～2.23	2.20～2.23	2.20～2.23
Porosity	%	20～26	20～27	20～27	20～27
Ash Content	%	≤0.2	≤0.2	≤0.2	≤0.2

Typical properties of nipples

Specifications	≤φ400	φ450-500	φ550	φ600-700
Specific Resistance (μΩM )	≤4.0	≤3.8	≤3.6	≤3.6
Flexural Strength (MPa)	18-24	17-25	20-28	20-28
astic Modulus (GPa)	≤18	≤18	≤18	≤18
Bulk Density (g/cm³)	1.76-1.84	1.78-1.84	1.79-1.86	1.79-1.86
Coefficient Of Thermal Expansion (106/℃)	0.9-1.3	0.9-1.2	0.9-1.1	0.9-1.1
Ash Content (%)	≤0.3	≤0.3	≤0.3	≤0.3

Current carrying capacity for UHP graphite electrodes

Current Capacity Of UHP Graphite Electrodes
Specifications		Current Capacity(A)		Current Density(A/cm²)
(inch)	(mm)	AC	DC	AC	DC
12	300	18,000-32,000	-	24-43	-
14	350	22,000-39,000	-	22-39	-
16	400	28,000-47,000	-	21-36	-
18	450	34,000-55,000	-	21-33	-
20	500	41,000-63,000	-	20-31	-
22	550	48,000-70,000	65,000-78,000	19-28	26-32
24	600	55,000-80,000	75,000-90,000	19-27	26-31
W	650	69,000-89,000	87,000-104,000	20-26	25-30
28	700	80,000-100,000	100,000-120,000	20-25	25-30

Product detail pictures:

Related Product Guide:

Our intention should be to fulfill our consumers by offering golden provider, superior price and superior quality for Bottom price Uhp Electrodes - UHP Grades Graphite Electrodes – Sungraf , The product will supply to all over the world, such as: belarus, Riyadh, Qatar, We are your reliable partner in international markets with the high quality products. Our advantages are innovation, flexibility and reliability which have been built during the last twenty years. We focus on providing service for our clients as a key element in strengthening our long-term relationships. Our continual availability of high grade products in combination with our excellent pre-sales and after-sales service ensures strong competitiveness in an increasingly globalized market.

Carbon Graphite Electrode

Edm Graphite Electrode

Graphite Electrode Companies

Graphite Electrode Usage

Ladle Furnace Graphite Electrode

Steel Making Graphite Electrode

Uhp 400 Graphite Electrode

Uhp 500 Graphite Electrode

Uhp 600 Graphite Electrode

Uhp 700 Graphite Electrode

This manufacturers not only respected our choice and requirements, but also gave us a lot of good suggestions, ultimately， we successfully completed the procurement tasks.